The present work aims at studying mechanical property of the S-glass reinforced along the epoxy matrix composite which are filled with alumina filler at 0, 5% and 10% wt. percentage fabricated through hand layup techniques which will be making it like hybrid. To understand mechanical and physical abilities of prepared composite; the density, the tensile, flexural, impact and hardness tests are considered for ASTM standards respectively. The results obtained from the investigation reveals that, as the Alumina filler loading was increased to 10% wt. percentage in the S-glass epoxy hybrid composite, the mechanical properties were improved. The SEM analysis of the fractured tensile specimen was conducted, which showed the breaking of the particles, fiber pull outs and fiber breakage, matrix /fiber debonding of composites.